Vergelijkende analyse van ASTM A105 en A105N: de verschillen begrijpen

In terms of material selection, it is usually a compromise between toughness and strength. The choice depends on applications, machinability, and weldability. As for ASTM A105, it is a plain carbon steel, while ASTM A105N represents normalized carbon steel. The heat treatment improves the mechanical properties of the component.

What is ASTM A105?

ASTM A105 is a specification for forged carbon steel piping components, such as flanges, fittings, and valves, used in pressure systems. It is designed for use in high-temperature and high-pressure applications. The material is characterized by its good mechanical properties and weldability, making it suitable for various industrial applications, including oil and gas, chemical processing, and power generation.

What is ASTM A105N?

ASTM A105N is similar to A105 but includes an “N,” indicating that the material has undergone normalization—a heat treatment process that refines the grain structure and relieves internal stresses. This treatment enhances the mechanical properties of the steel, making A105N particularly suitable for applications where improved strength and performance under stress are required, especially in low-temperature environments.

ASTM A105 VS A105N

Functie	ASTM A105	ASTM A105N
Materiaalsoort	Flanges, Fittings, Valves	Flanges, Fittings, Valves
Warmtebehandeling	Not normalized	Normalized
Mechanische eigenschappen	Standard properties	Enhanced properties
Toepassingen	General pressure systems	Pressure systems with high stress
Usage Temperature	Suitable for higher temps	Suitable for low temperatures
Internal Stress	May retain internal stress	Reduced internal stress

ASTM A105 Chemical Composition

Element	C	Si	Mijn	P	S	Ik	Kreeft	Ik	Ik	V
Composition, %	≤0,35	0.10~0.35	0.60～1.05	≤0,035	≤0,040	≤0,40	≤0,30	≤0,40	≤0,12	≤0,08

OPMERKING:

For each reduction of 0.01 % below the specified carbon maximum (0.35 %), an increase of 0.06 % manganese above the specified maximum (1.05 %) will be permitted up to a maximum of 1.35 %.
The sum of copper, nickel, chromium, molybdenum and vanadium shall not exceed 1.00 %.
The sum of chromium and molybdenum shall not exceed 0.32 %.

Mechanische vereisten

Element	Tensile Strength, min:	Min. Yield Point:	Reduction of area, min:	Hardheid, HB, max
ASTM A105	70,000 psi (485 MPa]	36,000 psi [250 MPa]	30% min	187

More information about ASTM A105 VS 105N:

https://www.quora.com/How-do-the-ASTM-A105-and-the-ASTM-A105N-piping-applications-differ

Verwante bronnen

Soorten zeskantbouten

Zeskantbouten, ook wel bekend als bouten met zeskantkop of zeskantbouten, zijn een van de meest gebruikte bevestigingstypen in de bouw, machinebouw en diverse industriële toepassingen. Deze bouten hebben een zeskantige zeskantkop die eenvoudig aan te draaien is met een sleutel of dop. De schroefdraad zorgt voor een stevige bevestiging in combinatie met een moer of in een tapgat.

Lees meer »

Flenspakkinggids: Types, materialen en toepassingen uitgelegd

Een flenspakking is een elastisch materiaal dat tussen de afdichtingsvlakken van twee flenzen wordt aangebracht. Het wordt gebruikt om oneffenheden op te vullen en lekkage van vloeistof of gas te voorkomen.

Lees meer »

Wat is een flensbout?

Een flensbout is een bevestigingsmiddel dat specifiek wordt gebruikt om twee flenzen met elkaar te verbinden. Het heeft een cilindrische behuizing, met aan de ene kant schroefdraad en aan de andere kant een kop; de schacht van de bout loopt niet taps toe. Bouten worden gemaakt van verschillende materialen, waarbij staal het meest wordt gebruikt in technische toepassingen. De tegenhanger van een bout is de moer, de bevestigingsmiddel met inwendige schroefdraad. Andere veelgebruikte bevestigingsmiddelen zijn schroeven (stelschroeven) en tapeinden.

Lees meer »